Table 2 Bursting strength loss of Mega-PK- and Mega-L-treated fabrics
From: Effects of biopolishing on the quality of cotton fabrics using acid and neutral cellulases
Sample no. | Concentration (%) | Temperature (°C) | Time (min) | Strength loss (%) | |
|---|---|---|---|---|---|
Mega PK | Mega L | ||||
1 | 0.5 | 45 | 40 | 1.7 | 1.5 |
2 | 0.5 | 55 | 40 | 2.5 | 2.2 |
3 | 0.5 | 65 | 40 | 4.1 | 3 |
4 | 0.5 | 45 | 50 | 4.9 | 3.2 |
5 | 0.5 | 55 | 50 | 5 | 3.3 |
6 | 0.5 | 65 | 50 | 5.8 | 4.1 |
7 | 0.5 | 45 | 60 | 5.8 | 4.9 |
8 | 0.5 | 55 | 60 | 6.6 | 5.8 |
9 | 0.5 | 65 | 60 | 7.4 | 5.9 |
10 | 1 | 45 | 40 | 8.2 | 6.6 |
11 | 1 | 55 | 40 | 9 | 7.4 |
12 | 1 | 65 | 40 | 10.7 | 8.2 |
13 | 1 | 45 | 50 | 11.5 | 9.1 |
14 | 1 | 55 | 50 | 12.4 | 9.9 |
15 | 1 | 65 | 50 | 13.2 | 10.7 |
16 | 1 | 45 | 60 | 14 | 11.5 |
17 | 1 | 55 | 60 | 14.8 | 11.6 |
18 | 1 | 65 | 60 | 15.6 | 12.4 |
19 | 1.5 | 45 | 40 | 16.5 | 12.5 |
20 | 1.5 | 55 | 40 | 17.3 | 13.2 |
21 | 1.5 | 65 | 40 | 18.1 | 14 |
22 | 1.5 | 45 | 50 | 18.9 | 14.8 |
23 | 1.5 | 55 | 50 | 20.6 | 15.6 |
24 | 1.5 | 65 | 50 | 22.2 | 16.5 |
25 | 1.5 | 45 | 60 | 23.1 | 17.3 |
26 | 1.5 | 55 | 60 | 23.9 | 18.1 |
27 | 1.5 | 65 | 60 | 24.7 | 18.9 |