Table 4 Abrasion resistance (mass loss) of biopolished cotton fabrics

From: Effects of biopolishing on the quality of cotton fabrics using acid and neutral cellulases

Sample no. Concentration (%) Temperature (°C) Time (min) Mass loss (mg) for Mega PK Mass loss (mg) for Mega L
100 cycles 250 cycles 500 cycles 750 cycles 1000 cycles 100 cycles 250 cycles 500 cycles 750 cycles 1000 cycles
Bleached 0.88 1.32 1.59 1.68 1.90 0.88 1.32 1.59 1.68 1.32
1 0.5 45 40 0.40 0.90 1.06 1.20 1.50 0.60 1.10 1.42 1.53 1.72
2 0.5 55 40 0.38 0.89 1.04 1.19 1.48 0.58 1.08 1.38 1.51 1.69
3 0.5 65 40 0.37 0.88 1.03 1.18 1.46 0.57 1.09 1.35 1.49 1.65
4 0.5 45 50 0.35 0.85 1.01 1.17 1.43 0.55 1.07 1.30 1.48 1.67
5 0.5 55 50 0.33 0.82 0.99 1.16 1.43 0.52 1.05 1.28 1.48 1.64
6 0.5 65 50 0.30 0.80 0.98 1.15 1.42 0.50 1.04 1.25 1.47 1.60
7 0.5 45 60 0.32 0.76 0.96 1.15 1.40 0.48 1.02 1.22 1.45 1.62
8 0.5 55 60 0.28 0.72 0.95 1.14 1.38 0.46 1.01 1.19 1.42 1.55
9 0.5 65 60 0.25 0.70 0.94 1.12 1.35 0.44 0.99 1.18 1.40 1.53
10 1 45 40 0.21 0.67 0.92 1.10 1.37 0.41 0.97 1.19 1.37 1.53
11 1 55 40 0.18 0.66 0.90 1.09 1.32 0.40 0.96 1.20 1.38 1.52
12 1 65 40 0.15 0.65 0.89 1.08 1.28 0.40 0.95 1.17 1.36 1.48
13 1 45 50 0.12 0.62 0.87 1.10 1.30 0.37 0.93 1.15 1.35 1.48
14 1 55 50 0.14 0.60 0.86 1.09 1.27 0.35 0.91 1.16 1.33 1.47
15 1 65 50 0.10 0.61 0.85 1.08 1.26 0.32 0.90 1.18 1.32 1.45
16 1 45 60 0.08 0.61 0.84 1.07 1.24 0.30 0.87 1.14 1.30 1.45
17 1 55 60 0.07 0.58 0.83 1.06 1.21 0.28 0.86 1.13 1.29 1.42
18 1 65 60 0.06 0.55 0.81 1.05 1.20 0.25 0.84 1.10 1.27 1.40
19 1.5 45 40 0.08 0.52 0.80 1.04 1.20 0.24 0.80 1.08 1.28 1.36
20 1.5 55 40 0.07 0.50 0.80 1.04 1.18 0.23 0.78 1.09 1.26 1.32
21 1.5 65 40 0.06 0.48 0.79 1.02 1.16 0.22 0.76 1.07 1.24 1.30
22 1.5 45 50 0.05 0.47 0.78 1.01 1.14 0.20 0.74 1.05 1.22 1.29
23 1.5 55 50 0.04 0.46 0.77 1.02 1.13 0.19 0.72 1.02 1.21 1.28
24 1.5 65 50 0.04 0.45 0.76 0.99 1.12 0.18 0.70 1.01 1.20 1.27
25 1.5 45 60 0.04 0.44 0.78 0.98 1.10 0.17 0.66 0.97 1.22 1.25
26 1.5 55 60 0.03 0.42 0.76 0.97 1.08 0.15 0.64 0.95 1.20 1.22
27 1.5 65 60 0.02 0.41 0.74 0.96 1.06 0.12 0.62 0.92 1.19 1.18
\